Comparison Of Bearing Material Technical Data 1 >>
Bearings
Technical data | Unit | GCr15 | 9Cr18 | Si3N4 | ZrO2 |
ρ Density | g/cm3 | 7.8 | 7.9 | 3.2 | 6 |
α Coefficient of expansion | 10-6/℃ | 11 | 17 | 3.2 | 10.5 |
E modulus of elastIcity | GPa | 208 | 200 | 320 | 210 |
µ Poisson ratio | 0.3 | 0.3 | 0.26 | 0.3 | |
HV Hardness | 800 | 700 | 1700 | 1300 | |
σb Flexural strength | Mpa | 2400 | 2600 | 900 | 1000 |
Compressive strength | Mpa | 3500 | 2000 | ||
Kc Impact strength | Nm/cm2 | 20 | 25 | 7 | 11 |
λ Thermal conductivity | W/mk | 30-40 | 15 | 3.5 | 2.5 |
Ω specific resistivity | mm2/m | 1 | 0.75 | 1018 | 1015 |
specific heat | J/KgK | 450 | 450 | 800 | 400 |
MAX permissible service temperature | ℃ | 120 | 150 | 1000 | 800 |
anti-corrossion | none | weak | strong | strong | |
NO.of stress circle(50% destroy) | 10*106 | 10*106 | 50*106 | 50*106 | |
Destroy model | peel off | peel off | peel off | peel off/break | |
Anti-magnetism | none | none | good | good | |
Dimension stability | not good | not good | good | good | |
Insulate properties | not good | not good | good | good |
Truck and Trailer Parts
Material | HDPE | PP | POM | PA 6 | PA 66 | PBT GF30 | PVDF | PPS | PTEE | PEEK | PI |
℃ Long-time working temp. | 90 | 100 | 110 | 100 | 100 | 120 | 150 | 230 | 260 | 260 | 300 |
(G/cm3 )ρ Density | 0.96 | 0.91 | 1.42 | 1.13 | 1.14 | 1.53 | 1.77 | 1.35 | 2.18 | 1.32 | 1.35 |
(Mpa) σs Tensile strength at yield | 25 | 30 | 70 | 85 | 80 | 50 | 75 | 25 | 95 | ||
(Mpa) σR Tensile strength at break | 35 | None | None | 13.5 | 4.6 | 116 | |||||
(Mpa)Hk Ball indentation harden | 50 | 80 | 170 | 160 | 170 | 190 | 80 | 190 | 30 | ||
(K J/m2) an Impact strength | None | None | None | None | None | 60 | None | 50 | None | None | 75 |
Coef. Of fliding frication | 0.29 | 0.3 | 0.34 | 0.38-0.45 | 0.35-0.42 | 0.24 | 0.3 | 0.08-0.1 | 0.3-0.38 | 0.3-0.38 | |
(µ/km) Slide wear | 11 | 4.6 | 0.23 | 0.9 | 21 | 0.3-0.38 | |||||
(℃) Vicat softening temp. | 130 | 165 | 175 | 220 | 260 | 225 | 170 | 280 | 327 | 343 | |
(℃) DSC/T g | -95 | -18 | -60 | 60 | 72 | 60 | -18 | 90 | -20 | 143 | |
(℃) Heat deflection temp. HDT/A | 42-49 | 65 | 124 | 75 | 100 | 210 | 95 | 110 | 55 | 140 | 368 |
(℃) Heat deflection temp. HDT/B | 70-85 | 105 | 170 | 190 | ﹥200 | 225 | 140 | 121 | 182 | ||
(℃) Max working temp. short time | 90 | 140 | 150 | 160 | 170 | 200 | 150 | 260 | 260 | 300 | 350 |
(10ˉ5/K) Coef. Of linear expansion | 13-15 | 17 | 10 | 8 | 8 | 3.5 | 13 | 5 | 12 | 5.0 | 4.9 |
(106Hz) Dielectric constant at 1 Mhz | 2.4 | 2.25 | 3.7 | 3.7-7 | 3.6-5 | 3.8 | 8 | 2.1 | 3.2-3.3 | 3.1 | |
(Ω·cm) Volume resistivity | ﹥1015 | ﹥1014 | ﹥1014 | 10¹⁴ | 10¹² | ﹥1013 | 10¹⁴ | 10¹³ | ﹥1016 | 10¹⁶ | 10¹⁷ |
Anti-hot water and alkali for washing | + | + | - | (+) | (+) | - | + | + | + | + | (+) |
Flammability UL94 | HB | HB | HB | HB | HB | HB | V0 | V0 | V0 | V0 | V0 |
Anti-weathering | - | - | - | - | - | - | + | - | + | - | (+) |