Properties Comparision of Ceramic Material >>
Bearings
Properties | Unit | B4C | Al2O3 | ZTA-20% | ZrO2 | Si3N4 | SiC |
Density | g/cm³ | 2.4~2.51 | 3.7~3.99 | 5.5 | 6 | 3.2 | 3.2 |
HV Hardness | Kg/mm | 2700~3200 | 2300~2700 | 1470~1500 | 1300~1500 | 1700~2700 | 2350~2450 |
Flexural strength | Mpa | 350~400 | 300~400 | 700 | 1000~1500 | 900 | 450~800 |
Indentation strength | Mpa | 1800~2500 | 2800~3500 | 2000 | 2000 | 3500 | 2250~3000 |
Impact strength | Mpa.m-3/2 | 6 | 2~4 | 5~6 | 11 | 7 | 4~5 |
Weber modulus | Gpa | >7 | >10 | >15 | >15 | >6 | |
Et Modulus of elasticity | Gpa | 407 | 260 | 210 | 320 | 410 | |
Poisson ratio | 0.2 | 0.23 | 0.3 | 0.26 | 0.16 | ||
Coaf. Ofexpansion | x10-6℃ | 4.5 | 6.5~8.6 | 9.4 | 10.5 | 3.2 | 4.3 |
Heat impact | △T℃ | 200 | 470 | 250 | 500 | 350 | |
Resistivity | Ω/c㎡ | 0.3~0.8 | >104~106 | >1010 | >1010 | >1014 | 100~2 |
Truck and Trailer Parts
Molecular formula | Contents % | Temperature | Anti-corrosion property |
CH3COOH | 80 | boiling | excellent |
CH3COOH + CH3CO | 50/80 | boiling | excellent |
H20 + NaCl | boiling | excellent | |
H2CO3 | boiling | excellent | |
Cu | 1400℃ | excellent | |
FoodAcid | boiling | excellent | |
Fruitjuice | boiling | excellent | |
HCl | 35 | 25℃ | good |
HCl + FaCl2 | boiling | good | |
HF | 25℃ | none resistant | |
HNO3 | 83 | 25℃ | good |
HNO3 + HCl | 80 + 20 | boiling | good |
H3PO4 | 85 | 25℃ | excellent |
KOH | 25℃ | excellent | |
NaCO3 + H2SO3 | 18/20 | 925℃ | excellent |
NaOH | 50 | boiling | excellent |
H2SO4 | 20 | 25℃ | excellent |
H2SO4 | 98 | 50℃ | good |
Al | 100 | 700℃ | excellent |
Zn | 100 | 500℃ | good |